FILM FACED PLYWOOD

According to the repeated using times,PUSENPLEX film faced plywood have below differently quality:

PUSEPLEX-HARDWOOD(☆☆☆☆☆)

Dynea film,Phenolic glue,full hardwood core(eucalyptus),can be used 15-20 times 

PUSEPLEX-COMBI(☆☆☆☆)

Brown film,WBP melamine glue,combi core(eucalyptus+poplar),can be used 8-12 times 

PUSEPLEX-POPLAR(☆☆☆)

Brown film,WBP melamine glue,poplar core,can be used 6-10 times 

PUSEPLEX-RECYCLE(☆☆)

Black film,WBP melamine glue,recycle core,can be used 1-4times 

Why customers choose PUSENPLEX ?

We provide premium quality, eco-friendly plywood sourced from sustainable wood. Our Film Faced Plywood ensures professional results, long service life, and excellent cost efficiency for contractors, builders, and manufacturers worldwide.

What options you can choose from PUSEN WOOD ?

No.1: you can choose differently film 

Dynea film paper-160-200g/㎡          Dynea is a well-known brand of impregnated paper in Finland, which is widely used in shuttering plywood production.

Phenolic film paper-160-200g/㎡       Excellent resistance to water, weather, chemicals and high temperatures, suitable for high-end construction formwork.

Melamine film paper-120-140 g/m²   Waterproof performance is better than MR glue, but not as good as phenolic resin glue, suitable for some mid-range building                                                                    formwork.

MR/UF film paper-100-120 g/m²       weakly waterproof, used for some simple packaging or non-load-bearing temporary structures.

No.2: you can choose differently glue:

WBP phenolic glue: 72 hours in boliling water

WBP melamine glue:24-48 hours in boliling water

Melamine glue:12-24 hours in boliling water

No.3: you can choose differently core:

Hardwood/combi/poplar/recycle

No.3: you can choose differently pressing

One time hot press one time cold press

Two tmes hot press one time cold press

Film Faced Plywood – Quality FAQ

 Delamination (Layer Separation)

Problem: Layers may separate under moisture or stress.
Cause: Poor adhesive, uneven pressing, or wet storage.
Our Solution:

• Use premium phenolic resin adhesives

• Control pressing temperature, pressure, and time

• Store plywood in dry, ventilated conditions

Surface Blisters or Bubbles

Problem: Small bubbles or blisters on the film surface.
Cause: Trapped moisture, uneven heat/pressure, or low-quality film.
Our Solution:

• Pre-dry veneers before lamination

• Maintain uniform pressing conditions

• Store film in dry, flat conditions

Film Peeling at Edges

Problem: Film lifting or peeling from plywood edges.
Cause: Insufficient adhesion, poor edge sealing, or rough handling.
Our Solution:

• Ensure full adhesion with proper pressing

• Seal edges carefully

• Handle plywood gently during transport

Warping or Bending

Problem: Plywood may twist, bend, or warp.
Cause: Uneven moisture, poor stacking, or sudden humidity changes.
Our Solution:

• Maintain consistent veneer moisture

• Store panels flat in ventilated areas

• Stack and transport properly

Cracks or Splits

Problem: Plywood may crack under stress or temperature changes.
Cause: Defective veneers, mechanical stress, rapid environmental change.
Our Solution:

• Use high-quality, defect-free veneers

• Handle carefully and acclimate to conditions before shipment

Uneven Gloss or Color

Problem: Surface may appear uneven in color or shine.
Cause: Inconsistent heat/pressure, film thickness variations, or premature UV exposure.
Our Solution:

• Apply uniform pressing and curing

• Use premium, consistent film materials

Our Film Faced Plywood is produced under strict quality control, with each step carefully monitored to guarantee superior durability, smooth finish, and reliable performance for construction and industrial projects worldwide.